Aging by moisture and/or temperature of epoxy/SiC composites: thermal and mechanical properties

J. Abenojar, M. Pantoja, M.A. Martínez, J.C. del Real-Romero

Journal of Composite Materials Vol. 49, nº. 24, pp. 2963 - 2975

Resumen:
The present work focuses on investigating the effects of moisture absorption on the mechanical and thermal properties of epoxy reinforced with percentage (by wt.) silicon carbide (nano and micro-metric) composites. In order to quantify the effect of moisture and temperature on aging, the specimens were exposed to three aging conditions for 30 days. Variations of Tg (glass transition temperature), water absorption, and mechanical properties were determined as a function of exposure time. In composite materials, aging depends on the exposure conditions, such as amount of absorbed water, temperature, and oxygen concentration. All these factors affect the thermal and mechanical properties. At room temperature and 95% relative humidity, plasticizing and swelling occur, with mechanical properties loss. At 60ºC and 5% relative humidity,, polymeric chains crosslink resulting in mechanical properties improvement; Tg and thermal conductivity increase. At 60ºC and 95% relative humidity, the time required to reach saturation decreases when compared to room temperature evaluated condition, as the exposure temperature increases.


Palabras Clave: Aging, epoxy, SiC, thermal properties, mechanical properties


Índice de impacto JCR y cuartil WoS: 1,242 - Q3 (2015); 2,300 - Q3 (2023)

Referencia DOI: DOI icon https://doi.org/10.1177/0021998314558496

Publicado en papel: Octubre 2015.

Publicado on-line: Noviembre 2014.



Cita:
J. Abenojar, M. Pantoja, M.A. Martínez, J.C. del Real-Romero, Aging by moisture and/or temperature of epoxy/SiC composites: thermal and mechanical properties. Journal of Composite Materials. Vol. 49, nº. 24, pp. 2963 - 2975, Octubre 2015. [Online: Noviembre 2014]


    Líneas de investigación:
  • *Materiales avanzados y nanotecnología

pdf Previsualizar
pdf Solicitar el artículo completo a los autores